[主观题]
在φ880轧机上热轧低碳钢板,轧制温度为1100℃,轧前厚为H=95mm,轧后厚为h=66.4mm,板宽为620mm,轧制速度为V=2.5m/s,此时的变形抗力σs=82Mpa,求轧制力。西姆斯公式Qp=f(R/h,ε)曲线。
在φ880轧机上热轧低碳钢板,轧制温度为1100℃,轧前厚为H=95mm,轧后厚为h=66.4mm,板宽为620mm,轧制速度为V=2.5m/s,此时的变形抗力σs=82Mpa,求轧制力。西姆斯公式Qp=f(R/h,ε)曲线。![在φ880轧机上热轧低碳钢板,轧制温度为1100℃,轧前厚为H=95mm,轧后厚为h=66.4mm,](https://img2.soutiyun.com/shangxueba/askkp/2022-12/23/1018/2022122314481688.png)